High-Quality PU leather lychee pattern artificial leather sofa fabric Manufacturer, Supplier

Crafted with a refined lychee-grain texture, this high-performance PU leather is designed for durability and aesthetic appeal in furniture applications. It features a substantial thickness of 1.2mm​ and a width of 140cm, ensuring reliable coverage and structural integrity. Weighing 500g/㎡, it offers a solid feel suitable for upholstery use. The base material utilizes a resilient non-woven/ spunlace fabric​ known for excellent toughness and recovery, making it ideal for areas subject to repeated compression, such as seating and backrests. This combination of texture, weight, and flexibility makes it an excellent choice for modern furniture that demands both style and long-term performance.

Product Description

Product Characteristic

This high-grade PU leather offers outstanding durability, featuring Martindale abrasion resistance ≥30,000 cycles (with premium variants exceeding 50,000 cycles). It demonstrates strong flex resistance, withstanding ≥150,000 cycles at room temperature and ≥80,000 cycles at -20℃ without cracking. The material boasts high peel strength (≥10 N/10mm), ensuring the PU layer remains firmly bonded to the substrate under repeated use.
With longitudinal tensile strength ≥18 MPa and transverse tensile strength ≥15 MPa, it is highly resistant to tearing. Its excellent elongation at break (≥120% longitudinal, ≥150% transverse) allows it to conform well to curved furniture designs. The surface is scratch-resistant, showing no visible marks under 5N load, and offers hydrolysis resistance ≥1000 hours (at 70°C, 95% humidity), making it suitable for humid indoor environments.
Frequently Asked Questions
How durable is this PU leather against daily wear?
The material features high-grade durability with Martindale abrasion resistance reaching over 30,000 to 50,000 cycles, making it ideal for long-term heavy use.
Does the PU leather crack in cold temperatures?
No, it is engineered for extreme flex resistance, withstanding up to 80,000 cycles at -20℃ without showing signs of cracking.
Is this fabric suitable for complex furniture shapes?
Yes, with a high elongation at break (up to 150% transversally), the fabric conforms exceptionally well to curved and intricate furniture designs.
How does the material perform in humid climates?
It offers superior hydrolysis resistance for over 1,000 hours at 70°C and 95% humidity, ensuring it won't degrade in humid indoor environments.
Is the surface resistant to scratches?
Yes, the surface is specifically treated to be scratch-resistant, leaving no visible marks even under a 5N load.
What is the strength of the bond between the leather layer and the base?
The material boasts a high peel strength of ≥10 N/10mm, ensuring the PU layer stays firmly attached to the substrate during repeated use.